P1511 Professional Architectural Handbuilding PF610 900-1300°C

Please select from the options above.
Architectural Handbuilding 900-1300°C
A cheaper alternative to T Material this excellent hand building body contains a high percentage of fine to medium molochite. This gives it superb sculptural qualities with very low shrinkage, approximately 6% at 1280°C. PF 610 is for potters who need a clay that does not warp under extreme conditions. It can be used with confidence to create even the largest pieces.
Firing Temperature - 900°C - 1300°C
% Shrinkage (w-f) - 6%
Texture (1 - Smooth to 10 - Coarse) - 6.
Fired Colour - Off White.
Weight 12.5kg